DIPON LuminaCast 6 Art Flow - Part B

Code: 7302/000250 7302/000500 7302/001000 7302/002500 Choose variant

Not rated

luminacast 6 art flow epoxidharz molds diponr (1)

7,79 € 13,01 € 20,83 € 47,80 € from 7,79 € 6,44 € excl. VAT 10,75 € excl. VAT 17,21 € excl. VAT 39,50 € excl. VAT from 6,44 € excl. VAT

(>5 pcs) (>5 pcs) (>5 pcs) (>5 pcs) Choose variant

Delivery to: 25/11/2024 25/11/2024 25/11/2024 25/11/2024 Choose variant Delivery offer
Mass
Chosen variant is not available. Reset selected parameters.

Detailed information

Product detailed description

Mixing ratio 2:1 by weight.
Casting height up to 20 mm and processing time up to 50 minutes depending on quantity and ambient temperature.
Unmolding possible after 16 - 24 hours (23 °C).
The next layer can be poured after approx. 12 - 16 hours (10 mm / 20 °C).
It creates an incomparably smooth and shiny surface.
The advanced formulation minimizes carbamate formation and ensures a flawless, blemish-free finish.
High Viscosity Consistency : In addition to LuminaCast 7 Design Flow, LuminaCast 6 Art Flow has the highest viscosity for the slowest flow properties.
For artists: Especially suitable for delicate floral designs, impressive geodes and projects where slow flow properties and perfect surface tension are important.
Superior glossy finish: Achieve brilliant, mirror-smooth surfaces on every project.

Maximum UV protection

The integration of UV absorbers and HALS additives ensures that LuminaCast perfectly protects your creations from yellowing and UV radiation damage.

Casting height up to 20 mm

Up to 20 mm (20°C) in a single pour, depending on the amount of material and ambient temperature.

Workability up to 55 mins

Extended workability provides ample time for mixing, pigmenting, and degassing the mixture (at 23°C, 200g, 20 mm).

Mixing ratio 2:1 by weight

Very easy mixing and calculation of the correct amount of individual components.

Applications

Highly transparent casts: Fabrication of transparent and aesthetically pleasing casts.
Jewelry: designing exquisite jewelry, elegant trays and complex geode coasters.
Sealing: creation and finishing of 3D floors, luxurious kitchen countertops and flawless epoxy table surfaces.
3D Flooring: elaboration of floors, including stunning 3D living room floors.
Geode art: creation of avant-garde geode artworks with a main focus on "resin art".
Petri-Art: Ideal system for Petri Art effects, combinable with colorants, especially "Alcohol-Inks".
Repair: self-leveling surface treatments and precise repair applications.

General Characteristics

Crystallization stable
Bio-based ingredients in the epoxy resin
Free from CoRAP and sVHC substances
State-of-the-art base amines and additives with particularly low yellowing tendencies
Mixing ratio: 2:1 by weight (A+B)
Pot life (23°C), 200 grams, 2 cm: approx. 50 min. (23°C- > 40°C)
Recommended material temperature (A+B): 20°- 24°C
Recommended ambient temperature: 20°C - 25°C
Dyn. Viscosity (mPa*s) 23°C: A 730 ± 50
Dyn. Viscosity (mPa*s) 23°C: B 4100 ± 50
Diamond Clear transparency
Layer thickness (20°C): 1 - 20 mm
0% VOC content
Excellent substrate wetting capability
Very low shrinkage (<0.1%)
Compatible with, e.g., wood, concrete, glass, metal, glass and carbon fiber fabrics, natural stone, quartz sand, marble, granite

Key Application Data

Pot life at 23°C (200 grams, 20 mm): approx. 50 min.
Time to max exothermy (tTmax) (23°C, 200 grams, 20 mm): approx. 100 min.
Mixing duration: 3-4 min. + transfer and another 3-4 min for a uniform mixture
Mixing ratio: 2:1 by weight (A+B)
Recommended casting height (20°C): 0.1 cm - 2.0 cm (1 - 20 mm)
Demoldable after (23°C): approx. 16 - 24 hrs.
Next layer pourable after: approx. 12 - 16 hrs. at 20°C, 10 mm
Minimum recommended mixing amount: 120 grams A+B

Application and Usage

Check the ambient temperature, as it's the most critical parameter alongside the casting volume. Successful application depends on room temperature and the amount/volume of the resin and hardener mix used. An excessively high room temperature can lead to a very strong exothermic reaction, resulting in yellowing, cracking, and vapor formation in the mixture.
Before use, perform a preliminary test for material compatibility to be painted/poured.
The recommended procedure for the most accurate measurement of all components is by weight, precisely weighing in a 100:50 or 2:1 weight parts ratio based on component (A). Even a slight deviation results in extended or non-occurring hardening. Adding too much hardener increases the material's elasticity and decreases its SHORE D hardness. Excess of component A results in a permanently sticky film, non-reversible due to polyaddition. The maximum deviation in the tolerance range is 0.1%.
Adhere to the recommended mixing time of three to four minutes, then pour into a clean container and mix again for three to four minutes to achieve a maximally homogeneous mixture.
Use the mixing container only once. Follow the recommended maximum mixing speed for both components, which is 300 rpm, preventing or minimizing the formation of air pockets during mixing. Manual mixing is recommended for smaller quantities up to approx. 1 kg. Due to its extended work time, it degasses excellently. We recommend using Allway Tools Helix for mixing.
To prevent resin seepage due to the prolonged curing time, ensure complete sealing of the mold. Suitable for this is the DIPON polypropylene tape, which can be easily separated from the mold after hardening. Optionally, a release wax can be used.

Cleaning

For cleaning used applicators, use acetone or universal thinner. Once the epoxy resin hardens, it can only be removed by sanding. Cleaning immediately after use is recommended.

Important Note:

Mixing transport containers (bottles/cans) A (resin) and B (hardener) will result in incomplete hardening and the corresponding incorrect result. Always weigh both components precisely.
The higher the room temperature and the larger the mixed quantity, the faster the exothermic reaction.

What is LuminaCast?

LuminaCast epoxy resin was developed with the aim of creating an unrivaled clear, UV-stabilized, and self-degassing system that's easy to use and covers the widest possible range of applications, particularly in the arts and crafts sector.
Special attention was given to achieving the highest possible carbamate resistance in all formulations by using the latest raw materials and adding hydrophobic additives. Additionally, besides the most up-to-date UV absorbers and light stabilizers, this system employs only slightly yellowing base amines in the hardener and especially UV-resistant additives. LuminaCast is designed for every application in the decorative sector, be it basic coatings, trays, furniture, or large volume casting.
With one resin and ten hardeners, you have maximum flexibility and can unleash your creative side!

Type	Dyn. Viscosity 23 °C (mPas)	**Proseccing time: 200g, 23 °C - 40 °C	Rec. Max. layer thickness	Purpose of use	UV protection
LuminaCast 1 Fast Set Primer	120 ± 50	cca 15 min	0,1 mm - 7 mm	Pre-treatment & priming	Excellent
LuminaCast 2 Coaster Cast	290 ± 50	cca 40 min	0,1 mm - 15 mm	Highly transparent embeddings	Excellent
LuminaCast 3 Crystal Flow	140 ± 50	cca 35 min	0,1 mm - 10 mm	Laminations & Art	Excellent
LuminaCast 4 Gem Flow	890 ± 50	cca 55 min	0,1 mm - 20 mm	Art & Embeddings	Excellent
LuminaCast 5 Radiant Flow	1330 ± 50	cca 60 min	0,1 mm - 20 mm	Art & Embeddings	Excellent
LuminaCast 6 Art Flow	4100 ± 50	cca 45 min	0,1 mm - 20 mm	Art & Embeddings	Excellent
LuminaCast 7 Design Flow	5500 ± 50	cca 50 min	0,1 mm - 20 mm	Art & Embeddings	Excellent
LuminaCast 8 Table Flow	70 ± 50	cca 180 min **500 grams, 9cm	20 mm - 50 mm	Thick film potting	Excellent
LuminaCast 9 Ocean Flow	50 ± 50	cca 240 min **500 grams, 9cm	30 mm - 100 mm	Thick film potting	Excellent
LuminaCast 10 Cell Flow	2500 ± 50	cca 50 min	0,1 mm - 20 mm	Art & Embeddings	Excellent

*Dynamic viscosity is measured at 23°C. A reduction in the material temperature is accompanied by a disproportionate increase in dyn. Viscosity. This is eminently important, especially when it comes to self-venting. Example. Viscosity Material temperature 23°C. 730 mPa*s, at 10°C Material temperature: approx. 10,000 mPa*s.
**The processing time is given for a mixture of 200 grams in a mixing cup (diameter 5 cm). Processing time = material temperature 23°C -> 40°C = doubling of the initial viscosity. The time to the max. exothermic temperature (tTMax) is usually twice the time of the prosecuting time.

LuminaCast 1 Fast Set Primer - Low viscosity, pot life, approx. 15 min., can be poured over after 60 - 120 min., ideal as primer / sealer for porous substrates such as wood
LuminaCast 2 Coaster Cast - Low viscosity, pot life approx. 40 min. ideal for decorative highly transparent embeddings and molds
LuminaCast 3 Crystal Flow - Especially low viscosity, pot life approx. 35 min. ideal for decorative highly transparent embeddings and molds
LuminaCast 4 Gem Flow Flow - Low viscosity, pot life approx. 55 min. e.g. for resin art with a higher viscosity, comparable to B20 JewelCast only more viscous
LuminaCast 5 Radiant Flow - Medium viscosity, pot life approx. 60 min. a.o. like LuminaCast 4 GemFlow, somewhat slower and slower flow properties due to higher viscosity
LuminaCast 6 Art Flow - High viscosity, pot life approx. 45 min. for painting techniques, resin art, worktops, sealers, similar to HoneyResin
LuminaCast 7 Design Flow - High viscosity, pot life approx. 50 min. Special flow properties due to actuator, similar to LuminaCast 6 ArtFlow, perceived thinner
LuminaCast 8 Table Flow - Low viscosity, pot life approx. 180 min. for large thick film castings e.g. for river tables, lamp production, larger castings in one casting
LuminaCast 9 Ocean Flow - Low viscosity, pot life approx. 240 min. for very large thick film castings e.g. for river tables, lamp production
LuminaCast 10 Cell Flow - Medium viscosity, pot life approx. 50 min. for cell effects, Petri Art, flower patterns, Resin Art, table tops, sealers etc.