Technical Data
Dynamic viscosity (resin A, 23 °C): 550 ± 50 mPa·s
Dynamic viscosity (hardener B, 23 °C): 75 ± 50 mPa·s
Processing time (23 °C, 500 grams, 90 mm): approximately 180 minutes (23 °C - 40 °C)
Recommended material temperature (A+B): minimum 20 °C, ideally 23 °C
Recommended ambient temperature: minimum 10 °C, ideally 12–19 °C
Next layer pourable after: approximately 28–36 hours (20 °C, 50 mm)
Sandable after: approximately 7–10 days (50 mm, 20 °C RT)
Recommended minimum casting height: 2 cm (20 mm)
Hardness after 7 days (23 °C): Shore D81
Heat resistance: approximately 65 °C
Maximum exotherm (tTmax, 23 °C, 500 grams, 90 mm): approximately 360 minutes
Mixing time: 3–4 minutes + repotting and an additional 3–4 minutes for a homogeneous mixture
Mixing ratio: 2:1 by weight or 100:40 by weight for higher strength
Recommended casting height (20 °C): 2.0 cm – 5.0 cm (20–50 mm)
Demoldable after (23 °C): (50 mm) approximately 72–96 hours
Minimum mixing quantity: recommended 120 grams (A + B)
Minimum casting height: recommended 20 mm